铝合金压铸常见问题及分析中英文对照版
更新时间:2024-03-26 05:49:01 阅读量: 综合文库 文档下载
- 压铸铝合金的金相分析推荐度:
- 相关推荐
常见压铸模具生产问题及分析
The common production problem and analysis of
die-casting moulds
压铸过程中金属液往外溅(跑铝)产生原因 The cause reason of molten metal splash when die casting.
1. 定模间合模不严密,间隙较大 Cover halves close imprecisely, and have big gap.
2. 锁模力不够 The mould clamming force is not enough. 3. 压铸机动,定模安装板不平行 The die casting machine is
flexible ,and the mounting plate of cover half(fixed die) is not parallel.
4. 支板跨度大,压射力致使套板变形,产生喷料。Support span(跨度) is large, and the injection pressure(force) bring about the cleading(保热套(汽锅的);护罩;护壁板(隧道的))deformation , engendering(使产生;)产生molten metal spouting(喷射) .
调整方法 method of adjustment 1.重新安装模具 reinstall the mould
2.加大锁模力 increase the mould clamming force
3.调整压铸机,使动、定模安装板相互保持平行 adjust the die-casting machine, ensure the mounting plate of fixed die(cover half) and moving die maintain mutual(共同的;相互的,彼此的) parallel。
4.在动模上增加支板,增加套板的刚度。Add support plate on the movable mould , increase the stiffiness(硬、刚度,rigidity,hardness) of the cleading
影响压射头(压力喷嘴)使用寿命的因素,主要因素有:The factors influencing the working life of the pressure nozzle(喷嘴;管口;鼻) jet ,main factors :
1.压射头(喷嘴)本身的材料、质量;The material and quality of the nozzle jet
2.压射头与压射料筒之间的配合间隙;The fit clearance of the press charging(炉料;装料) barrel and jet nozzle
3.模具安装时与压射料筒的同心度;The concentricity of the mould and press charging barrel while installing 4.冷却问题;cooling problem
5.选用优质压射头润滑油等。Select and use the superior nozzle jet lube(lubrication) etc.
缺陷名:产品表面起皱
Defect name : surface wrinkling of the product
(一)症状:产品表面形成的不规则褶皱,主要出现在壁较薄的前段部分,如所示。
(1)Symptom: The irregular folds(皱褶;折痕) emerging on the surface of product ,mainly appearing the thinner wall ,as show :
可以看到射出的细小铝颗粒和褶皱。Can see the small aluminium granule 原因:由于吸入了脱模剂和压缩空气,被封闭在前段的气压较高,把产品表面顶起而导致这一现象的发生Reason: owing to indrawing the release agent or compressed air,air preasure being sealed up in the forepart is high then jack up the surface of the product and result in this phenomenon
解决方案:排气彻底,清除多余的脱模剂。调整高速高压区的位置以防止溶液降温 solution :exhaust thoroughgoing,eliminate the extra mold lubricant ,adjust the position of the high speed ,high preasure to prevent the melton metal cooling down 缺陷名defect name :起皱(二)wrinkle(2)
症状:镶件附近的圆柱状部分,表面的皮膜出现起皱现象起皱的表面部分,根据发生状态有差异。Symptom: the cylinder part around the insert ,the surface membrana demalis appearing crumpling up ,it is different according to the occuring condition
在靠近镶件的拐角处,出现与镶件平行的褶皱。在离拐角稍远处,表面皮膜起皱部分有细小的铝颗粒聚集,呈粉末状附着在表面起皱的断面可以观察到起皱导致的凹凸,细小的铝颗粒被压碎后嵌入褶皱里。 Near the corner of the insert ,appearing the parellel wrinkle with the insert .a little far away from the corner .the surface membrana demalis can see the
aluminium granule gathered ,appearing in power attached to the surface cut can see the concave-convex , the wee aluminium granule inbedding into the wrinkle after crushed
原因:在模具温度低时进行铸造容易b发生此现象。铝液在流道流淌时前锋冷却,形成 氧化皮膜,在距离浇口较远的突起部分凝固,由于压力增大在表面形成褶皱。Reason: when die casting with the low temperature of the mould is easy to occur this ,the molten aluminum flowing in the passageway the forepart cooled and form oxide membrana demalis ,then occur solidification at the tuber fruther as due to the high pressure appearing wrinkle on the surface .
解决方案:对模具进行预热,在设定的温度条件下进行生产是很重要的,将模具温度设定在适当的范围。Solution :preheat of the mould and produce under the setted temperature ,should control the temperature of the mold in aopportune scope .
换导柱以及导套时一定要注意尺寸变化,尤其是长时间使用但是没有回火或者测量的模具,一定要检查模具的尺寸,包括模板平行度、孔直线度、孔内外径是否变化。一般情况下基准尺寸会变化。Exchange the guide pillar or guide sleeve should notice the change in the size ,especially the mould that is used for a long time without tempering or measured including the mould plate parallel, straightness ,change of internal and external diameter.Nomaly the reference dimention will exchange .
锌压铸件毛坯看不到麻点,电镀前抛光就出现麻点,这是怎么回事?这是锌压铸件最易出现的问题之一。Zink die pressed casting blank is no hard spot ,but when polish before electroplating the hard spot occur. What’s up ?
要注意 notice :
1.原材料的质量(纯净度);the quality of the material (degree of purity) 2.熔化时的精炼除气除渣;rifine to degassing and deslagging when melting .
3.压铸时速度、压力 的调整(特别是皮下气孔等缺陷);adjust the speed and pressure when die-casting
4.抛光时摩擦 的压力和温度不要太高。The pressure and temperature of the friction can not be too high .
中国压铸企业主要集中在长三角、珠三角、京津唐、东北重庆西安等西部、东北等地区。
在生产汽车配件一样壳体时抽芯处老是出现凹槽请问下有些什么原因? 1.浇注系统、排溢系统开设问题;gating system ,ejecting system 2.压铸工艺参数选择问题;die-casting technological parameters choosing problem
3.原材料质量等。The material quality problem
正在阅读:
铝合金压铸常见问题及分析中英文对照版03-26
2016年钟秀勇民法模拟题(钟秀勇2016年4月10日)03-29
2019秋苏教译林版小学英语四年级上册五六单元测试题09-14
大学综英第三版第四册课后翻译答案09-12
课程与教学论12-26
婴儿推车项目可行性研究报告立项申请报告模板 - 图文12-18
2018年(牛津译林版)英语六年级下册unit1-2第一二单元测试卷(含听06-09
中医体质调护案例10-07
县供销社项目建设工作总结报告范文08-04
- 多层物业服务方案
- (审判实务)习惯法与少数民族地区民间纠纷解决问题(孙 潋)
- 人教版新课标六年级下册语文全册教案
- 词语打卡
- photoshop实习报告
- 钢结构设计原理综合测试2
- 2014年期末练习题
- 高中数学中的逆向思维解题方法探讨
- 名师原创 全国通用2014-2015学年高二寒假作业 政治(一)Word版
- 北航《建筑结构检测鉴定与加固》在线作业三
- XX县卫生监督所工程建设项目可行性研究报告
- 小学四年级观察作文经典评语
- 浅谈110KV变电站电气一次设计-程泉焱(1)
- 安全员考试题库
- 国家电网公司变电运维管理规定(试行)
- 义务教育课程标准稿征求意见提纲
- 教学秘书面试技巧
- 钢结构工程施工组织设计
- 水利工程概论论文
- 09届九年级数学第四次模拟试卷
- 压铸
- 中英文
- 铝合金
- 对照
- 常见问题
- 分析
- 外文翻译
- 地源热泵空调与传统空调方式初投资及运行费用比较
- 吴敬琏:改革面临四大阻力
- PLC练习题1-5文档
- 关于情感教学在初中历史教学中的运用分析
- 主诉检察官办案责任制是什么意思
- MFC单文档应用程序练2
- C程序设计(第四版)谭浩强 - 课后习题答案 - 共11章 - xin
- XX年护理年度工作总结范文
- 陈琦 - 图文
- 初三历史第五次月考试题及答案
- 成语故事大全
- 缩孔、缩松的预测 - 图文
- 委托银行(金融机构)划缴税款三方协议书
- 化妆品生产企业卫生许可管理办法征求意见稿
- 《市政规划与管理》复习资料 整理版
- 数据库原理及应用模拟试题 综合版
- 河海大学文天学院第二届水利达人秀策划书
- 2018小升初语文课堂体验模拟试卷二
- 高压运行维修练习(第九次增订)(带答案)