不锈钢等钢材知识 - 图文

不锈钢管尺寸对照表(美标ANSI-日标JIS-德标DIN-英标BS-韩标KS) Dimensions for ASME/ANSI Standards Nominal pipe Size(NPS) 8 1/4 13.7 10 3/8 17.1 15 1/2 21.3 20 3/4 26.7 25 1 33.4 0.54 0.675 0.84 1.05 1.32 1.66 1.90 2.38 2.88 3.50 4.00 4.50 5.56 6.62 8.62 10.75 12.75 14 16 18 20 22 24 26 28 30 32 Outside Diameter Unit:mm B16.9 B16.28 B36.10 Nominal Wall Thickness Sch5s SCH10S Sch20 Sch30 Sch40 STD Sch80 XS - - 1.65 1.65 - - - - - - - - - - - - - - Sch160 XXS - - 1.85 2.24 2.24 3.02 3.02 - 1.85 2.31 2.31 3.20 3.20 - 1.65 2.11 1.65 2.11 1.65 2.77 1.65 2.77 1.65 2.77 1.65 2.77 2.11 3.05 2.11 3.05 2.11 3.05 2.11 3.05 2.77 3.40 2.77 3.40 2.77 3.76 3.40 4.19 3.96 4.57 3.96 4.78 4.19 4.78 4.19 4.78 4.78 5.54 4.78 5.54 5.54 6.35 - - - - - - - - 2.41 2.77 2.77 3.73 3.73 4.78 7.47 2.41 2.87 2.87 3.91 3.91 5.56 7.82 2.90 3.38 3.38 4.55 4.55 6.35 9.09 2.97 3.56 3.56 4.85 4.85 6.35 9.70 3.18 3.68 3.68 5.08 5.08 7.14 10.15 3.18 3.91 3.91 5.54 5.54 8.74 11.07 4.78 5.16 5.16 7.01 7.01 9.53 14.02 4.78 5.49 5.49 7.62 7.62 11.13 15.24 4.78 5.74 5.74 8.08 8.08 - - 32 1.1/4 42.2 40 1.1/2 48.3 50 2 60.3 65 2.1/2 73.0 80 3 88.9 90 3.1/2 101.6 100 4 125 5 150 6 200 8 250 10 300 12 350 14 400 16 450 18 500 10 550 22 600 24 650 *26 700 *28 750 *30 800 *32 114.3 141.3 168.3 219.1 273.0 323.8 355.6 406.4 457 508 559 610 660 711 762 813 4.78 6.02 6.02 8.56 8.56 13.49 17.12 - - 6.55 6.55 9.53 9.53 15.88 19.05 7.11 7.11 10.97 10.97 18.26 21.96 6.35 7.04 8.18 8.18 12.70 12.70 23.01 22.23 6.35 7.80 9.27 9.27 15.09 12.70 28.58 25.40 6.35 8.38 10.13 9.53 17.48 12.70 33.32 25.40 7.92 9.53 11.13 9.53 19.05 12.70 35.71 - 7.92 9.53 12.70 9.53 21.44 12.70 40.49 - 7.92 11.13 14.27 9.53 23.83 12.70 45.24 - 9.53 12.70 15.09 9.53 26.19 12.70 50.01 - 9.53 12.70 - 9.53 28.58 12.70 53.98 - 9.53 14.27 17.48 9.53 30.96 12.70 59.54 - - - - - - - - - - - - - 9.53 - 9.53 - 9.53 - 9.53 - 12.70 - 12.70 - 12.70 - 12.70 - - - - - 不锈钢管无缝钢管及焊管标准 产品名称 不锈钢管 不锈钢管 不锈钢管 规格、型号 Φ6～630x 1～50mm Φ6～630x 1～50mm Φ6～630x 1～50mm 标准名称 流体输送用不锈钢管 结构用无缝不锈钢管 锅炉、热交换器用不锈钢管 标准号 GB/T14976-2002 GB/T14975-2002 GB13296-91

不锈钢焊管 Φ219～1200x 3～20mm 流体输送用不锈钢管 GB12770-2002 各国不锈钢管材质对照表 GB1220不锈钢材质标准 日本 JIS德国 DINl7440。。 NFA35-572。。 原苏联 AISI。。 BS970Part4。。 不锈钢材DINl7224不锈钢NFA35-576-582 TOCT5632不锈ASTM不锈BSl449part2不质标准 材质标准 NFA35-584不锈钢材质标准 钢材质标准 锈钢材质标准 钢材质标准 248Sl6 302S25 304S15 304S12 305S19 316S16 316S12 320S17 X12CrNi188 X5CrNi189 X2CrNi189 X5CrNi1911 X5CrNiMo1810 X2CrNiMo1810 Z10CN18.09 Z6CN18.09 Z2CN18.09 Z8CN18.12 Z6CND17.13 Z2CN17.12 l2Xl7T9AH4 20Xl3H4T9 12X18H9 08X18H10 03X18H11 12X18H12T 08X17H13M2T 03X17H13M2 08X17H13M2T 10X17H13M2T 08X18H10T 12X18H10T 美国 英国 法国 lCrl8Mn8Ni5N SUS202 202 S20200 2Crl3Mn9Ni4 lCrl8Ni9 0Crl8Ni9 SUS302 302 30200S SUS304 304 S30400 304L S30403 00Crl8Ni10 SUS304L lCrl8Nil2Ti SUS305 305 S30500 lCr25Ni20Si2 SUS3l0S 3l0S S3l008 0Crl8Ni2Mo2Ti SUS3l6 3l6 S3l600 00Crl7Ni4Mo2 SUS3l6L 0Crl8Ni2Mo2Ti lCrl8Ni2Mo2Ti 0Crl8Ni9Ti 1Crl8Ni9Ti

3l6L S3l603 X10CrNiMoTi1810 Z6CNDT17-12 Z6CNT18.10 SUS321 32l S32l00 321S12 321S20 X10CrNiTi189 32l XCrNiTi189 不锈钢管无缝钢管材质化学成分

不锈钢管无缝钢管材质化学成分

不锈钢无缝钢管（0Cr18Ni9、 0Cr25Ni20、0Cr18Nil0Ti、00Cr17Nil4M02、0Crl 8Nil2M02Ti、1Crl 8Ni9Ti）

标准：

GB/T14975---------中国国家标准 GB/T14976---------中国国家标准 GB13296-------- ---中国国家标准

用途： 用于机械结构、流体管道、锅炉过热器、热交换器、冷凝器、催 化管等。 主要生产钢管牌号： 0Cr18Ni9、 0Cr25Ni20、0Cr18Ni10Ti、00Cr17Nil4M02、0Crl 8Ni12M02Ti、1Cr18Ni9Ti等。 机械性能 牌号 0Cr18Ni9(304) 0Cr25Ni20(310S) 0Cr18Ni10Ti(321) 00Cr17Ni14Mo2(316L) 0Cr18N12Mo2Ti 1Cr18Ni9Ti(321) 化学成份 牌号 C 0Cr18Ni9 0Cr25Ni20 0Cr18Ni10Ti 00Cr17Ni14Mo2 0Cr18N12Mo2Ti 1Cr18Ni9Ti 0.07 0.08 0.08 0.03 0.08 0.12 Si 1.00 1.00 1.00 1.00 1.00 1.00 Mn ≤ 2.00 2.00 2.00 2.00 2.00 2.00 0.035 0.035 0.035 0.035 0.035 0.035 0.30 0.30 0.30 0.30 0.30 0.30 P S 化学成分 Ni 8.00-11.00 19.00-22.00 9.00-12.00 12.00-15.00 11.00-14.00 8.00-11.00 Cr 17.00-19.00 24.00-26.00 17.00-19.00 16.00-18.00 16.00-19.00 17.00-19.00 2.01.8抗拉强度（Mpa） ≥ 520 520 520 480 530 550 205 205 205 175 205 205 35 35 35 35 35 35 屈服强度（Mpa） 伸长率（％） 结构用不锈钢无缝钢管的牌号和化学成分

组织 序类型 号 1 牌 号 化学成分(质量分数)(％) C ≤0.07 Si ≤Mn ≤P ≤S ≤Ni 8.00～C 17.00～19.00 17.00～19.00 18.00～20.00 17.00～19.00 17.00～19.00 16.00～18.50 16.00～Mo 其 他 OCr18Ni9 1.00 2.00 0.035 0.030 11.00 ≤≤≤≤8.00～2 lCrl8Ni9 ≤O.15 1.00 2.00 O.035 O.030 lO.00 3 奥氏 ≤≤≤≤8.00～00Crl9NilO ≤0.030 1.00 2.00 0.035 O.030 12.00 ≤≤≤≤9.00～ 体型 4 0Crl8Ni10Ti ≤0.08 1.00 2.O0 O.035 O.030 12.00 ≤≤≤≤9.00～ Ti≥5C％ 5 OCrl8NillNb ≤O.08 1.00 2.00 0.035 0.030 13.00 ≤≤≤≤10.00～ 2.00～3.00 2.00～Nb≥10C％ 6 0Crl7Nil2M02 ≤0.08 1.00 2.00 O.035 O.030 14.00 ≤≤≤12.00～ 7 00Crl7Nil4M02 ≤0.030 ≤

1.00 2.00 O.035 0.030 15.00 8 OCrl8Nil2M02Ti ≤0.08 ≤≤≤≤11.00～18.oo 16.00～19.00 16.00～19.00 16.oo～19.00 16.00～19.00 3.00 1.80～2.50 1.80～2.50 2.50～3.50 2.50～3.50 Ti 5C％～O.70 Ti 5(C％-0.02) ～0.80 Ti5C％～O.70 Ti 5(C％-0.02) ～0.80 Ti 5(C％～ O.02) ～0.80 3.00～4.00 3.00～4.00 1.00 2.00 0.035 O.030 14.00 ≤≤≤≤11.00～9 1Crl8Nil2M02Ti ≤O.12 1.00 2.00 O.035 O.030 14.00 ≤≤≤≤11.00～lO 0Crl8Nil2M03Ti ≤0.08 1.00 2.00 O.035 0.030 14.00 ≤≤≤≤11.00～11 1Crl8Ni12Mo3Ti ≤O.12 1.00 2.00 O.035 0.030 14.00 12 1Crl8Ni9Ti ≤0.12 ≤≤≤≤8.00～17.00～19.oo 18.00～20.00 18.00～20.00 12.00～14.00 16.00～18.00 11.50～13.50 12.00～14.00 1.00 2.00 O.035 0.030 11.00 ≤≤≤≤11.00～13 0Cr19Nil3M03 ≤O.08 1.00 2.00 0.035 O.030 15.00 ≤≤≤≤11.00～14 00Crl9Nil3M03 ≤0.030 1.00 2.00 0.035 O.030 15.00 15 铁素 16 体型 马氏 17 体型 18 OCrl3 ≤O.08 ≤≤≤≤ 0.60 0.80 0.035 O.030 ≤≤≤≤ lCrl7 ≤O.12 0.75 1.00 O.035 0.D30 ≤≤≤≤ 1Crl3 ≤O.15 O.16～1.00 1.00 0.035 0.030 ≤≤≤≤ 2Crl3 0.25 1.00 1.00 O.035 O.030 注：*残余元素Ni≤O.60。 表6-20结构用不锈钢无缝钢管的尺寸允许偏差 热轧(挤、扩)钢管 尺寸／mm 允许偏差／mm 普通级 ±1.25 ±l ±1.5 外径D 较高级 冷拔(轧)钢管 尺寸／mm 10≤D≤30 30 D>5 +15 -12.5 +20 -15 ±12.5 壁厚 >3 ≤3 ±O.9％ ±14％ +12％ -10％ ±0.8％ +12％ -10％ ±lO％ 土O.40 ±O.30 允许偏差／mm 普通级 ±O.30 较高级 土O.20 68≤D≤159 外径D 159 <15 壁厚 ≥15 注：供机械加工用钢管应在合同中注明，根据需方要求，经供需双方协议，可规定机械加工余量。 表6-2l结构用不锈钢无缝钢管的力学性能

力学性能 组织类型 序号 牌 号 推荐热处理制度 ób／MPa ó0. 2／MPa δ5(％) ≥ l 2 3 4 5 6 奥氏体型 OCr18Ni9 lCrl8Ni9 00Crl9Ni10 OCrl8Nil0Ti 0Crl8NillNb OCrl7Nil2M02 lOl0～1150℃，急冷 1010～1150℃，急冷 1010～1150℃，急冷 920～1150℃，急冷 980～1150cC，急冷 1010～1150℃，急冷 520 520 480 520 520 520 480 530 530 530 530 520 520 480 370 410 410 470 205 206 175 206 205 205 175 205 205 205 205 205 205 175 180 245 205 215 35 35 35 35 35 35 35 35 35 35 35 35 35 35 22 20 20 19 7.93 7.90 7.93 7.95 7.98 7.98 7.98 8.00 8.00 8.10 8.10 7.90 7.98 7.98 7.70 7.70 7.70 7.70 密度(g／cm3) 7 00Cr17Nil4M02 1010～1150℃。急冷 8 OCr18Mil2M02Ti 1000～1100℃，急冷 9 lCrl8Nil2M02Ti 1000～1100℃，急冷 10 oCr18Nil2M03Ti 1000～1100℃，急冷 11 1Crl8Nil2M03Ti 1000～1100℃。急冷 12 1Cr18Ni9Ti 1000～1100℃，急冷 10lO～1150℃，急冷 13 0Crl9Nil3M03 14 00Crl9Ni13M03 lOlO～1150℃，急冷 铁索体型 15 16 17 18 OCrl3 lCrl7 lCrl3 2Crl3 780～830℃，空冷或缓冷 780～850℃，空冷或缓冷 800～900℃，缓冷 800～900℃，缓冷 马氏体型 注：1.热挤压管的抗拉强度允许降低20MPa。 2.钢管经热处理并酸洗交货。凡经整体磨、镗或经保护气氛热处理的钢管，可不经酸洗交货。 3.供机械加工用钢管可不经酸洗交货。

合金结构钢相应的合金无缝钢管的力学性能和化学成分 合金结构钢（GB/T3077-1999）的牌号和化学成分(1) 序 统一数 牌 号 号 字代号 l A00202 20Mn2 2 A00302 30Mn2 Mn 3 A00352 35Mn2 4 A00402 40Mn2 5 A00452 45Mn2 Mn 6 A00502 50Mn2 化学成分(质量分数)(％) C Si Mn Cr Mo Ni B V 其他 钢组 0.17-0.24 0.17-0.37 1.40-1.80 0.27-0.34 0.17-0.37 1.40-1.80 0.32-0.39 0.17-0.37 1.40-1.80 0.37-0.44 0.17-0.37 1.40-1.80 0.42-0.49 0.17-0.37 1.40-1.80 0.47-0.55 0.17-0.37 1.40-1.80 0.17-0.24 0.17-0.37 1.30-.60 0.24-0.32 1.10-1.40 1.10-1.40 0.32-0.40 1.10-1.40 1.10-1.40 0.39-0.45 1.10-1.40 1.10-1.40 MnV 7 A01202 20MnV 8 A10272 27siMn siMn 9 A10352 35siMn 10 A10422 42siMn 0.07-0.12

ll A14202 20SiMn2MoV 0.17-0.23 0.90-1.20 2.20-2.60 0.30-0.40 SiMn- 12 A14262 25SiMn2MoV 0.22-0.28 0.90-1.20 2.20-2.60 0.30-0.40 MoV 13 A14372 37SiMn2MoV 0.33-0.39 0.60-0.90 1.60-1.90 0.40-0.50 14 A70402 40B B 15 A70452 45B 16 A70602 50B MnB Mn MoB MnVB 17 A71402 40MnB 18 A71452 45MnB 19 A72202 20MnMoB 20 A73152 15MnVB 21 A73202 20MnVB 0.37-0.44 0.17-0.31 0.60-0.90 0.42-0.49 0.17-0.37 0.60-0.90 0.47-0.55 0.17-0.37 0.60-0.90 0.37-0.44 0.17-0.37 1.10-1.40 0.42-0.49 0.17-0.37 1.10-1.40 0.16-0.22 0.17-0.37 0.90-1.20 0.20 -0.30 0.05-0.12 0.05-0.12 0.05-0.12 0.0005-0.0035 0.0005-0.0035 0.0005-0.0035 0.0005-0.0035 0.0005-0.0035 0.0005-0.0035 0.12-0.18 0.17-0.37 1.20-1.60 0.17-0.23 0.17-0.37 1.20-1.60 0.0005-0.0035 0.07-0.12 0.005-0.0035 0.07-0.12 合金结构钢的牌号和化学成分(2) 钢组 序 号 22 统一数 字代号 A73402 牌 号 化学成分(质量分数)(％) C Si Mn Cr Mo Ni B V 其他 Ti0.04-0.10 Ti0.04-0.10 40MnVB 0.37-0.17-1.10-0.44 0.37 1.40 0.17-0.17-1.30-0.24 0.37 1.60 0.22-0.2Q-1.30-0.28 0.45 1.60 0.0005-0.05-0.0035 0.10 0.0005-0.0035 0.0005-0.0035 23 MnTiB 24 A74202 20MnTiB A74252 25MnTiBRE 25 A20152 15Cr 0.12-0.17-0.40-0.70-0.18 0.37 0.70 1.00 0.12-0.17-0.40-0.70-0.17 0.37 0.70 1.00 0.18-0.17-0.50-0.70-0.24 0.37 0.80 1.00 0.27-0.17-0.50-0.80-0.34 0.37 0.80 1.10 0.32-0.17-0.50-0.80-0.39 0.37 0.80 1.10 0.37-0.17-0.50-0.80-0.44 0.37 0.80 1.10 0.42-0.17-0.50-0.80-0.49 0.37 0.80 1.10 0.47-0.17-0.50-0.80-0.54 0.37 0.80 1.10 0.35-1.00-0.30-1.30-0.43 1.30 0.60 1.60 26 Cr 27 A20153 15CrA A20202 20Cr 28 A20302 30Cr 29 35Cr 30 Cr 3l A20402 40Cr A20452 45Cr 32 A20502 50Cr CrSi 33 QlMo 34 A21382 A30122 38Crsi 12CrMo 0.08-0.17-0.40-0.40-0.40-

0.15 0.37 0.70 0.70 0.55 35 A30152 15CrMo 0.12-0.17-0.40-0.80-0.40-0.18 0.37 0.70 1.10 0.55 0.17-0.17-0.40-0.80-0.15-0.24 0.37 0.70 1.10 0.25 0.26-0.17-0.40-0.80-0.15-0.34 0.37 0.70 1.10 0.25 0.26-0.17-0.40-0.80-0.15-0.33 0.37 0.70 1.10 0.25 0.32-0.17 0.40-0.80-0.15-0.40 -0.37 0.70 1.10 0.25 0.38-0.17-0.50-0.90-0.15-0.45 0.37 0.80 1.20 0.25 0.08-0.17-0.40-0.30-0.25-0.15 0.37 0.70 0.60 0.35 0.30-0.17-0.40-1.00-0.20-0.38 0.37 0.70 1.30 0.30 0.08-0.17-0.40-.0.900.25-0.15 0.37 0.70 -1.20 0.35 0.22-0.17-0.40-1.50-0.25-0.29 0.37 0.70 1.80 0.35 0.22-0.17-0.50-2.10-0.90-0.29 0.37 0.80 2.50 1.10 0.35-0.20-0.30-1.35-0.15-0.42 0.45 0.60 1.65 0.25 0.37-0.17-0.50-0.80-0.44 0.37 0.80 1.10 0.47-0.17-0.50-0.80-0.54 0.37 0.80 1.10 0.12-0.17-1.10-0.40-0.18 0.37 1.40 0.70 0.17-0.17-0.90-0.90-0.23 0.37 1.20 1.20 0.37-0.17-0.90-0.90-0.45 0.37 1.20 1.20 0.17-0.90-0.80-0.80-0.23 1.20 1.10 1.10 0.22-0.90-0.80-0.80-0.28 1.20 1.10 1.10 0.27-0.90-0.80-0.80-0.34 1.20 1.10 1.10 36 A30202 20CrMo 37 A30302 30CrMo 38 QlMo 39 A30303 30CrMoA A30352 35CrMo 40 A30422 42CrMo 0.15-0.30 0.10-0.20 0.15-0.30 0.15-0.30 0.30-0.50 0.10-0.20 0.10-0.20 41 A31122 12CrMoV 42 A31352 35CrMoV QMoV 43 A31132 12CrlMoV 44 A31253 25Cr2MoVA 45 CrMoAL A31263 25CrMolVA Al0.70-1.10 46 A33382 38CrMoAl 47 CrV 48 A23402 40CrV A23503 50CrVA 49 A22152 15CrMn CrMn 50 A22202 20CrMn 51 A22402 4CrMn CrMnSi 52 A24202 20CrMnSi 53 A24252 25CrMnSi CrMnS54 i 55 A24302 A24303 30CrMnSi 30CrMnSiA 0.28-0.90-0.80-0.80-

0.34 1.20 1.10 1.10 56 A24353 350MnSiA 0.32-1.10-0.80-1.10-0.39 1.40 1.10 1.40 CrMnMo 57 A34202 20CrMnMo 0.17-0.17-0.90-1.10-0.20-0.23 0.37 1.20 1.40 0.30 0.37-0.45 58 A34402 40CrMnMo

常用钢管板材的理论计算公式大全

圆钢重量（公斤）=0.00617×直径×直径×长度

方钢重量（公斤）=0.00785×边宽×边宽×长度

六角钢重量（公斤）=0.0068×对边宽×对边宽×长度

八角钢重量（公斤）=0.0065×对边宽×对边宽×长度

螺纹钢重量（公斤）=0.00617×计算直径×计算直径×长度

角钢重量（公斤）=0.00785×（边宽+边宽-边厚）×边厚×长度

扁钢重量（公斤）=0.00785×厚度×边宽×长度

无缝钢管重量（公斤）=0.02466×壁厚×（外径-壁厚）×长度

六方体体积的计算

公式① s20.866×H/m/k 即对边×对边×0.866×高或厚度

各种钢管(材)重量换算公式

无缝钢管的重量=0.25×π×(外径平方-内径平方)×L×钢铁比重其中：π = 3.14 L=钢管长度 钢铁比重取7.8 所以， 钢管的重量=0.25×3.14×(外径平方-内径平方)×L×7.8 * 如果尺寸单位取米（M）,则计算的重量结果为公斤（Kg）

钢的密度为： 7.85g/cm3 （注意：单位换算）

钢材理论重量计算

钢材理论重量计算的计量单位为公斤（ kg ）。其基本公式为：

W（重量，kg ）=F(断面积 mm2)×L(长度，m)×ρ(密度，g/cm3)×1/1000

常用数据

钢的比重(密度）： 7.8g/cm

不锈钢比重（密度）：7.78g/cm

铝的比重（密度）： 2.7g/cm

锌比重（密度）： 7.05g/cm

几种金属型材理论重量简易计算公式：

1、 角钢：每米重量=0.00785×（边宽+边宽—边厚）×边厚

2、 管材：每米重量=0.02466×壁厚×（外径—壁厚）

3、 圆钢：每m重量=0.00617×直径×直径 (螺纹钢和圆钢相同）

4、 方钢：每m重量=0.00786×边宽×边宽

5、 六角钢：每m重量=0.0068×对边直径×对边直径

6、 八角钢：每m重量=0.0065×直径×直径

7、 等边角钢：每m重量=边宽×边厚×0.015

8、 扁钢：每m重量=0.00785×厚度×宽度

9、 无缝钢管：每m重量=0.02466×壁厚×(外径-壁厚)

10、电焊钢：每m重量=无缝钢管

11、钢板：每㎡重量=7.85×厚度

12、黄铜管：每米重量=0.02670×壁厚×（外径-壁厚）

13、紫铜管：每米重量=0.02796×壁厚×（外径-壁厚)

14、铝花纹板：每平方米重量=2.96×厚度

15、有色金属密度：紫铜板8.9 黄铜板8.5 锌板7.2 铅板11.37

16、有色金属板材的计算公式为：每平方米重量=密度×厚度

17、方管: 每米重量=(边长+边长)×2×厚×0.00785

18、不等边角钢 ： 每米重量=0.00785×边厚(长边宽+短边宽--边厚)

19、工字钢 ：每米重量=0.00785×腰厚[高+f（腿宽-腰厚）]

20、槽钢： 每米重量=0.00785×腰厚[高+e（腿宽-腰厚）]

结构用无缝钢管结构管的材质标准及化学性能

结构管 结构用无缝钢管（GB/T8162-1999） 结构用无缝钢管 标准： GB/T8621---------中国国家标准 用途： 适用于一般结构，机械结构用无缝钢管。 主要生产钢管牌号： 10、20、35、45、16Mn、12CrMo、15CrMo、12Cr1MoV等。 机械性能： 标准 牌号 10 20 35 GB/T8162 45 16Mn 12CrMo 15CrMo 12Cr1MoV 化学成份： 标准 牌号 10 20 GB/T8162 35 45 16Mn 化学成分 C Si Mn P、S Cu Ni Mo / / / / / Cr ≤0.15 ≤0.25 ≤0.25 ≤0.25 ≤0.25 抗拉强度(MPa) ≥ 335 ≥ 390 ≥ 510 ≥ 590 ≥ 490 ≥ 410 ≥ 440 ≥ 490 屈服强度(MPa) ≥ 205 ≥ 245 ≥ 305 ≥ 335 ≥ 325 ≥ 265 ≥ 295 ≥ 245 伸长率(%) ≥ 24 ≥ 20 ≥ 17 ≥ 14 ≥ 21 ≥ 24 ≥ 22 ≥ 22 0.07～0.14 0.17～0.37 0.35～0.65 ≤0.035 ≤0.25 ≤0.25 0.17～0.24 0.17～0.37 0.35～0.65 ≤0.035 ≤0.25 ≤0.25 0.32～0.40 0.17～0.37 0.50～0.80 ≤0.035 ≤0.25 ≤0.25 0.42～0.50 0.17～0.37 0.50～0.80 ≤0.035 ≤0.25 ≤0.25 0.12～0.20 0.20～0.55 1.20～1.60 ≤0.035 ≤0.25 ≤0.25 12CrMo 0.08～0.15 0.17～0.37 0.40～0.70 ≤0.035 ≤0.25 ≤0.30 0.40～0.55 0.40～0.70

15CrMo 0.12～0.18 0.17～0.37 0.40～0.70 ≤0.035 ≤0.25 ≤0.30 0.40～0.55 0.80～1.10 12Cr1MoV 0.08～0.15 0.17～0.37 0.40～0.70 ≤0.035 ≤0.25 ≤0.30 0.25～0.35 0.90～1.20

锅炉管材质标准及化学成分机械性能

低中压锅炉管/高压锅炉管力学性能 纵向力学性能 标准 GB3087-1999 10 20 20G 20MnG 25MnG 15MoG GB5310-1995 20MoG 12CrMoG 15CrMoG 12Cr2MoG 12Cr1MoVG 12Cr2MoWVTib 化学成分 化学成分 标准 牌号 10 C Si Mn P≤ S≤ Cr ≤0.15 ≤0.25 - Mo - V - Ti - B - W - 牌号 抗拉强度(MPa) 屈服点（MPa）≥ 伸长率（%）≥ 冲击功(J)≥ 333-475 392-588 410-550 ≥415 ≥485 450-600 ≥415 410-560 440-640 450-600 470-640 540-735 196 245/226 245 240 275 270 220 205 235 280 255 345 24 20 24 22 20 22 22 21 21 20 21 18 - - 35 35 35 35 35 35 35 35 35 35 0.07-0.17-0.35-0.14 0.37 0.65 0.17-0.17-0.35-0.24 0.37 0.65 0.17-0.17-0.35-0.24 0.37 0.65 0.17-0.17-0.70-0.24 0.37 1.00 0.22-0.17-0.70-0.30 0.37 1.00 0.12-0.17-0.40-0.20 0.37 0.80 0.15-0.17-0.40-0.25 0.37 0.80 0.08-0.17-0.40-0.15 0.37 0.70 GB3087-1999 0.035 0.035 20 0.035 0.035 - - - - - 20G 0.030 0.030 - - - - - 20MnG 0.030 0.030 - - - - - - 25MnG GB5310-1995 15MoG 0.030 0.030 - - 0.25-0.35 0.44-0.65 - - - - 0.030 0.030 - - - - - 20MoG 0.030 0.030 - - - - - 12CrMoG 0.030 0.030 0.40-0.40-0.70 0.55 - - - - - - - - 15CrMoG 0.12-0.17-0.40-0.030 0.030 0.80-0.40-

0.18 0.37 0.70 12Cr2MoG 0.08-≤0.40-0.030 0.030 1.10 0.55 2.00-0.90-2.50 1.20 - - - - 0.15 0.50 0.70 0.08-0.17-0.40-0.15 0.37 0.70 12Cr1MoG 0.030 0.030 0.90-0.25-0.15-01.20 0.35 .30 - - - 12Cr2MoWV0.08-0.45-0.45-TiB 0.15 0.75 0.65 0.030 0.030 1.60-0.50-0.28-00.08-00.002-00.30-02.10 0.65 .42 .18 .18 .55 流体输送用不锈钢无缝钢管的牌号和化学成分 组织序类型 号 1 牌 号 化学成分(质量分数)(％) C ≤Si Mn ≤≤P ≤S ≤Ni Cr M0 Ti 其他 0Cr18Ni9 8.oo～17.00～19.00 0.07 1.00 2.00 O.035 O.030 11.00 ≤≤≤≤≤2 00Crl9NilO 8.00～18.00～20.00 22.0～24.00 O.03c 1.00 2.00 O.035 O.030 12.00 ≤≤≤≤≤12.0～ 3 OCr23Nil3 O.08 1.00 2.00 O.035 O.030 15.00 ≤≤≤≤≤ 4 oCr25Ni20 19.00～24.00～26.00 O.08 1.oo 2.00 O.035 O.030 22.00 ≤≤≤≤≤ 5wc～0.07 5 0Crl8Ni10Ti 9.00～17.00～19.00 O.08 1.00 2.oo O.035 0.030 12.00 ≤≤≤≤≤ ≥5wc 6 OCrl8Ni11Nb 9.00～17.00～19.00 O.08 1.00 2.00 O.035 O.030 13.00 ≤≤≤≤≤ Nb≥lOwc 7 OCrl7Nil2M02 奥氏体 8 00Crl7Ni14M02 型 9 OCrl9Nil3M03 10.00～16.00～2.00～18.50 3.00 O.08 1.0D 2.00 0.035 O.030 14.00 ≤≤≤≤≤ 12.00～16.0～2.00～18.00 3.00 0.030 1.00 2.00 O.035 0.030 15.00 ≤≤≤≤≤ 11.00～18.00～3.00～20.00 4.00 O.08 1.00 2.00 O.035 0.030 15.00 ≤≤≤≤≤ lO 00Crl9Nil3M03 11.00～18.00～3.00～20.00 4.00 O.030 1.00 2.00 O.035 0.030 15.00 ≤≤≤≤≤ 11 OCrl8Nil2M02Ti 11.00～16.00～1.80～19.00 2.50 O.08 1.00 2.00 O.035 0.030 14.00 ≤≤≤≤≤5wc～0.70 5(wc～O.02) ～O.80 5wc～O.70 12 1Crl8Nil2M02Ti 11.oo～16.00～1.80～19.00 2.50 0.12 1.00 2.00 O.035 O.030 14.00 ≤≤≤≤≤ 13 0Crl8Ni12Mo3Ti 11.00～16.00～2.50～19.00 3.50 16.0～19.00 0.08 1.00 2.00 O.035 O.030 14.00 ≤≤≤≤≤1.00～ 14 lCrl8Ni12Mo3Ti 2.50～5(wc_o.02) 3.50 ～0.80 O.12 1.00 2.00 O.035 O.030 14.00

15 0Cr18Ni12Mo2C ≤≤≤≤≤11.00～17.00～1.20～19.00 2.75 O.08 1.00 2.00 O.035 O.030 14.00 Gul.0～2.50 Cu1.00～2.50 ≤≤≤≤≤12.00～17.00～1.20～16 00Cr18Ni14Mo2Cu2 O.03( 1.oD 2.00 0.035 0.030 16.00 19.00 2.75 ≤≤≤≤≤8.00～17.00～19.00 12.00～14.oo 5(wc～17 1Crl8Ni9Ti O.12 1.00 2.oo O.035 O.030 11.00 ≤≤≤≤≤ 0.02) ～0.08 铁素 体型 奥氏 18 0Cr13 0.08 O.60 0.80 O.035 O.030 ① 体.铁 19 OCr26Ni5Mo2 索体型 ≤≤≤≤≤3.00～23.00～1.00～28.00 3.00 O.08 1.00 1.50 O.035 O.030 6.00 表6-29流体输送用不锈钢无缝钢管的力学性能 力学性能 组织类型 序号 牌 号 推荐热处理制度 ób／MPa 密度／(g／cm3) óO.2／MPa δ5(％) ≥ 1 2 3 4 5 6 7 8 奥氏体型 9 10 ll 12 13 14 15 OCrl8Ni9 00Cr19Nil0 0Cr23Nil3 OCr25Ni20 OCrl8Nil0Ti OCrl8Ni11Nb OCrl7Ni12M02 00Cr17Nil4Mo2 OCrl9Nil3M03 00Cr19Nil3M03 OCrl8Nil2M02Ti 1Crl8Ni12M02Ti 0Cr18Ni12Mo3Ti 1Crl8Nil2M03Ti 0Crl8Nil2M02Cu2 1010～1150℃，急冷 1010～1150℃，急冷 1030～1150℃，急冷 1030～1150℃，急冷 920～1150℃，急冷 980～1150℃，急冷 1010～1150℃，急冷 1010～1150℃，急冷 lOlO～1150℃，急冷 1010～1150℃，急冷 1000～1100℃，急冷 1000～1100℃，急冷 1000～1100℃，急冷 1000～1100℃，急冷 1010～1150℃，急冷 1010～1150℃，急冷 1000～1100℃，急冷 520 480 520 520 520 520 520 480 520 480 530 530 530 530 520 480 520 205 175 206 205 205 206 205 175 205 175 205 205 205 205 205 180 205 180 390 35 35 35 35 35 35 35 35 35 35 35 35 35 35 35 35 35 22 18 7.93 7.93 7.98 7.98 7.95 7.98 7.98 7.98 7.98 7.98 8.00 8.00 8.10 8.10 7.98 7.98 7.90 7.70 7.80 16 00Cr18Nil4M02Cu2 17 18 铁素 体型 奥氏体 19 1Crl8Ni9Ti OCrl3 OCr26Ni5M02 780～830℃，空冷或缓冷 370 ≥950℃，急冷 590 一铁素

体型 注：1.热挤压管的抗拉强度允许降低20Mpa. 2.钢管经热处理并酸洗交货。凡经整体磨、镗或经保护气氛热处理的钢管，可不经酸洗交货。 3.根据需方要求，在合同中注明，可测定钢管的屈服强度。